Magnesium ingot

Magnesium ingot is a kind of light metal raw material for producing magnesium alloy, aluminum alloy and other series products. Magnesium ingot has high specific strength, high specific stiffness, good shock absorption and good cutting performance.

The Magnesium Ingot Uses

Magnesium ingots are less dense metal, with a density two-thirds that of aluminum. As a metal material with low density, magnesium ingot is widely used in aerospace industry, military industry, transportation, 3C field and so on. With the development of science and technology and the emergence of new technology and new process, the application of magnesium ingot will be more and more extensive.


The Specification of Mg Ingot

Mg Ingot
Brand Chemical composition

Brand Mg Fe Si Ni Cu Al Cl Mn Others
Mg99.98 99.98 0.002 0.003 0.002 0.0005 0.004 -- 0.002 0.02
Mg99.96 99.96 0.004 0.004 0.0002 0.002 0.006 0.003 0.003 0.04
Mg99.95 99.95 0.004 0.005 0.0007 0.003 0.006 0.003 0.01 0.05
Mg99.9 99.90 0.04 0.01 0.001 0.004 0.02 0.005 0.03 0.10
Mg99.8 99.80 0.05 0.03 0.002 0.02 0.05 0.005 0.06 0.20



Magnesium Ingot for Sale
HS Code: 8104110000
Brand: ZHENXIN
Origin: Henan, China

Production Capacity: 5,000MT/Month





The Production Process of Magnesium Ingot
 Dolomite is broken by crusher qualified material (30-40mm), sintering by rotary kiln, calcined into calcine white.
 It is cooled by a cooling machine, then ground into powder by a ball mill and pressed into balls by a ball press.
 After crushing, it is evenly mixed with ferrosilicon powder (containing 75% silicon) and fluorite powder to make a group.
 Put into the heat-resistant stainless steel reduction tank, placed in the reduction furnace, reduction at 1200-1250℃ and 1.33Pa vacuum degree of vacuum to make crude magnesium.
 After solvent refining, casting and surface treatment, finished magnesium ingot was obtained.