The Samurai Challenge - Not a San Mai, Not a Katana

*The original title was "San Mai Katana", but after so many people wanting to correct it and so many others just wanting to show off or bother me, I thought it would be fun to change the title saying what this sword is not.
The truth is that I did it to have fun and participate in a game, I don't care what they call it. ;)

Hey guys!

Today I bring something new: my first sword!

It would take a little longer to make this piece, but as "The Samurai Challenge" came up, I ended up anticipating it.

In order to be able to build it on time and without delaying my orders too much, I opted for a simpler constitution than a traditional katana. The fulltang shape guarantees a lot of robustness, and has a certain practicality in assembly. To put the traditional binding on the grip, I opted for san mai steel with manganese phosphate treatment, which will protect the carbon in the center from any type of oxidation.

I did the partial roughing to keep the side in a brute forge finish, because I think it creates a nice contrast against the mirrored stainless steel and black carbon.

The heat treatment was done with clay, in order to keep the back soft and reduce the chance of fracture as in traditional katanas.

I like pieces that mix refined and rustic details, I identify with that, and I think this piece is a good example of the combination.

Thank you for your attention!
Hope you like it!


Olá pessoal!

Trago hoje uma novidade: minha primeira espada!

Demoraria um pouco mais para fazer essa peça, mas como surgiu o "The Samurai Challenge" acabei antecipando.

Para conseguir construir ela dentro do prazo e sem atrasar muito minhas encomendas optei por uma constituição mais simples que uma katana tradicional. O shape fulltang garante muita robustez, e tem certa praticidade na montagem. Para colocar a amarração tradicional na empunhadura optei pelo aço san mai com tratamento no fosfato de manganês, que vai proteger o carbono no centro de qualquer tipo de oxidação.

Fiz o desbaste parcial para manter a lateral com acabamento brute forge, porque acho que ele cria um belo contraste contra o inox espelhado e o carbono negro.

O tratamento térmico foi feito com argila, afim de manter o dorso macio e diminuir a chance de fratura como nas katanas tradicionais.

Gosto de peças que mistura detalhes refinados com rústicos, me identifico com isso, e acho que essa peça é um bom exemplo da combinação.

Obrigado pela atenção!
Espero que gostem!