Fused then Slumped! But How Did it Go? Fused Glass Project - Part 2

It started as a pot melt, that became a feature in this fused glass bowl. It was a long process, especially the strip construction. But after all that, how did it work out?

Don't go away! Follow this adventure and wait till the end to see the final result.

📌This is Part 2 of this project. You can find Part 1 here -    • A Pot Melt What? A Bowl! That's Potty...  

🔴 Join Membership -    / @rocketroseart  
This will open YouTube in a browser so you can join.

🔴 Subscribe -    / @rocketroseart  

⏱️ Chapters ⏱️
0:00 Intro & Details
2:21 Cutting
9:57 Coldworking
13:02 Fire Polish
13:50 Slump

📌 Other Glass Fusing Videos
Pot Melt -    • Monster of a Pot Melt! What is It? Fu...  
Pot Melt Bowl Part 1 -    • A Pot Melt What? A Bowl! That's Potty...  
🎥 Fused Glass Playlists -    / @rocketroseart  

💥 Fire Polish Firing Schedule
1 - 222 C (432 F) up to 535 C (995 F), hold 60 minutes
2 - 333 C (632 F) up to 725 C (1337 F), hold 20 minutes
3 - Full down to 482 C (900 F), hold 60 minutes
4 - 65 C (149 F) down to 425 C (797 F), no hold
5 - 132 C (270 F) down to 371 C (700 F), no hold

💥 Slump Firing Schedule
1 - 167 C (333 F) up to 620 C (1148 F), no hold
2 - Full down to 482 C (900 F), hold 60 minutes
3 - 65 C (149 F) down to 425 C (797 F), no hold
4 - 132 C (270 F) down to 371 C (700 F), no hold